Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 0.953 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 0.24 g/10min |
| melt mass-flow rate | | ISO 1133 | 20 g/10min |
| melt mass-flow rate | | ISO 1133 | 1.1 g/10min |
| Environmental stress cracking resistance | | ASTM D1693 | 500 hr |
| FNCT | | ISO 16770 | 12.0 hr |
| Melt flow ratio | | | 90.0 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 61 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Blow molding melt temperature | | | 180to225 °C |
| Blow molding mold temperature | | | 20to30 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ISO 527-2 | 26.0 MPa |
| Tensile strain | Yield | ISO 527-2 | 10 % |
| Flexural modulus | | ISO 178 | 1150 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 4.5 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179 | 10 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 46.0 °C |
| vicat | | ISO 306 | 125 °C |
| melting temperature | | ISO 11357-3 | 130 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare