PE Copolymer LITEN BB 85 F Unipetrol RPA, s.r.o.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Unipetrol RPA, s.r.o./LITEN BB 85 F |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 10 kJ/m² |
| -30°C | ISO 179 | 4.5 kJ/m² |
| hardness | Test Condition | Test Method | Unipetrol RPA, s.r.o./LITEN BB 85 F |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 61 |
| Supplementary Information | Test Condition | Test Method | Unipetrol RPA, s.r.o./LITEN BB 85 F |
|---|---|---|---|
| Blow molding mold temperature | 20to30 °C | ||
| Blow molding melt temperature | 180to225 °C |
| Mechanical properties | Test Condition | Test Method | Unipetrol RPA, s.r.o./LITEN BB 85 F |
|---|---|---|---|
| Tensile strain | 屈服 | ISO 527-2 | 10 % |
| tensile strength | 屈服 | ISO 527-2 | 26.0 MPa |
| Flexural modulus | ISO 178 | 1150 MPa |
| physical property | Test Condition | Test Method | Unipetrol RPA, s.r.o./LITEN BB 85 F |
|---|---|---|---|
| density | 23°C | ISO 1183 | 0.953 g/cm³ |
| melt mass-flow rate | 190°C/5.0kg | ISO 1133 | 1.1 g/10min |
| Environmental stress cracking resistance | F50 | ASTM D1693 | 500 hr |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 0.24 g/10min |
| FNCT | 50°C | ISO 16770 | 12.0 hr |
| Melt flow ratio | 21.6/2.16 | 90.0 | |
| melt mass-flow rate | 190°C/21.6kg | ISO 1133 | 20 g/10min |
| Thermal performance | Test Condition | Test Method | Unipetrol RPA, s.r.o./LITEN BB 85 F |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 130 °C | |
| vicat | ISO 306 | 125 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 46.0 °C |