LLDPE

LLDPE L2009FA Thailand Siam Chemical

Usages:
Bags films industrial applications mixing agricultural applications heavy packaging bags
Compare

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
turbidity	38.0μm	ASTM D1003	15 %
gloss	38.0μm	ASTM D2457	53

thermal performance	Test Method	Test Result
Melting temperature	ASTM D2117	122 °C
Vicat softening temperature	ASTM D1525	102 °C
Brittle temperature	ASTM D746	<-70.0 °C

Physical properties	Test Condition	Test Method	Test Result
Environmental stress cracking resistance	50°C,25%Igepal,Compression Molded,F50	ASTM D1693B	>1000 hr
melt mass-flow rate	190°C/2.16kg	ASTM D1238	1.0 g/10min
density		ASTM D1505	0.919 g/cm³

film	Test Condition	Test Method	Test Result
Secant modulus	2%Secant,MD:38μm	ASTM D882	260 MPa
tensile strength	MD:Break,38μm	ASTM D882	37.3 MPa
	tensile strength	TD:Yield,38μm	ASTM D882	13.7 MPa
	tensile strength	tensile strength	MD:Yield,38μm	ASTM D882	11.8 MPa
Secant modulus	2%Secant,TD:38μm	ASTM D882	272 MPa
Elmendorf tear strength	TD:38μm	ASTM D1922	370 g
Elmendorf tear strength	Elmendorf tear strength	MD:38μm	ASTM D1922	150 g
Dart impact	38μm	ASTM D1709	130 g
elongation	TD:Break,38μm	ASTM D882	840 %
elongation	elongation	MD:Break,38μm	ASTM D882	620 %
tensile strength	TD:Break,38μm	ASTM D882	34.3 MPa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.