LLDPE L2009FA Thailand Siam Chemical
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | Thailand Siam Chemical/L2009FA |
|---|---|---|---|
| Secant modulus | 2%正割,TD:38µm | ASTM D882 | 272 MPa |
| tensile strength | TD:屈服,38µm | ASTM D882 | 13.7 MPa |
| Elmendorf tear strength | MD:38µm | ASTM D1922 | 150 g |
| elongation | MD:断裂,38µm | ASTM D882 | 620 % |
| Elmendorf tear strength | TD:38µm | ASTM D1922 | 370 g |
| tensile strength | MD:屈服,38µm | ASTM D882 | 11.8 MPa |
| MD:断裂,38µm | ASTM D882 | 37.3 MPa | |
| Dart impact | 38µm | ASTM D1709 | 130 g |
| tensile strength | TD:断裂,38µm | ASTM D882 | 34.3 MPa |
| elongation | TD:断裂,38µm | ASTM D882 | 840 % |
| Secant modulus | 2%正割,MD:38µm | ASTM D882 | 260 MPa |
| optical performance | Test Condition | Test Method | Thailand Siam Chemical/L2009FA |
|---|---|---|---|
| Haze ratio | 38.0µm | ASTM D1003 | 15 % |
| gloss | 38.0µm | ASTM D2457 | 53 |
| physical property | Test Condition | Test Method | Thailand Siam Chemical/L2009FA |
|---|---|---|---|
| density | ASTM D1505 | 0.919 g/cm³ | |
| Environmental stress cracking resistance | 50°C,25%Igepal,模压成型,F50 | ASTM D1693B | >1000 hr |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 1.0 g/10min |
| Thermal performance | Test Condition | Test Method | Thailand Siam Chemical/L2009FA |
|---|---|---|---|
| vicat | ASTM D1525 | 102 °C | |
| melting temperature | ASTM D2117 | 122 °C | |
| brittle temperature | ASTM D746 | <-70.0 °C |