Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D955 | 1.4 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | 内部方法 | 52to62 |
| Shore hardness | | 内部方法 | 62 |
| Shore hardness | | 内部方法 | 57 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | FMVSS302 | 51 mm/min |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ozone resistance | | ASTM D518/1149 | NoCracking |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ASTM D412 | 2.07 Mpa |
| Tensile stress | | ASTM D412 | 3.45 Mpa |
| tensile strength | | ASTM D412 | 5.52 Mpa |
| elongation at break | | ASTM D412 | 700 % |
| tear strength | | ASTM D624 | 26.3 kN/m |
| compression set | | ASTM D395B | 15 % |
| compression set | | ASTM D395B | 38 % |
| Tensile stress | | ASTM D412 | 1.38 Mpa |
| aging | Test Condition | Test Method | Test Result |
|---|
| Change rate of tensile strength in air | | ASTM D573 | 140 % |
| Change rate of ultimate elongation in air | | ASTM D573 | 130 % |
| Change rate of hardness (Shore) in the air | | ASTM D573 | 2.0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| brittle temperature | | ASTM D746 | -63.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.