PP Matrixx FPP1A20CC USA The Matrixx Group
0
- Properties:Fillerglass fiber reinforced material20%filler by weight
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 4.0 g/10min | |
| density | ASTM D792 | 1.05 g/cm³ | |
| Shrinkage rate | 内部方法 | 0.20to0.50 % | |
| density | ASTM D792 | 1.05 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 4.0 g/10min | |
| Shrinkage rate | 内部方法 | 0.20to0.50 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB | |
| UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | Yield | ASTM D638 | 63.4 MPa |
| Flexural modulus | ASTM D790 | 3590 MPa | |
| tensile strength | Yield | ASTM D638 | 63.4 MPa |
| Flexural modulus | ASTM D790 | 3590 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 64 J/m | |
| ASTM D256 | 64 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 157 °C | |
| ASTM D648 | 143 °C | ||
| RTI Str | UL 746 | 65.6 °C | |
| Heat distortion temperature | ASTM D648 | 157 °C | |
| ASTM D648 | 143 °C | ||
| RTI Str | UL 746 | 65.6 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.