PP Matrixx FPP1A20CC USA The Matrixx Group
--
--
Filler, glass fiber reinforced material, 20%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | USA The Matrixx Group/Matrixx FPP1A20CC |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 64 J/m |
| Mechanical properties | Test Condition | Test Method | USA The Matrixx Group/Matrixx FPP1A20CC |
|---|---|---|---|
| Flexural modulus | ASTM D790 | 3590 MPa | |
| tensile strength | 屈服 | ASTM D638 | 63.4 MPa |
| flammability | Test Condition | Test Method | USA The Matrixx Group/Matrixx FPP1A20CC |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | USA The Matrixx Group/Matrixx FPP1A20CC |
|---|---|---|---|
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 4.0 g/10min |
| Shrinkage rate | MD：3.18mm | 内部方法 | 0.20to0.50 % |
| density | ASTM D792 | 1.05 g/cm³ |
| Thermal performance | Test Condition | Test Method | USA The Matrixx Group/Matrixx FPP1A20CC |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 143 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 157 °C | |
| RTI Str | UL 746 | 65.6 °C |