Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
Water absorption rate | | ISO 62 | 0.50 % |
density | | ISO 1183 | 1.40 g/cm³ |
spiral flow length | | 内部方法 | 18.0 CM |
Shrinkage rate | | ISO 294-4 | 1.0 % |
Shrinkage rate | | ISO 294-4 | 0.40 % |
Water absorption rate | | ISO 62 | 0.40 % |
hardness | Test Condition | Test Method | Test Result |
---|
Shore hardness | | ISO 868 | 86 |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
Tensile modulus | | ISO 527-2 | 7500 Mpa |
tensile strength | | ISO 527-2 | 135 Mpa |
Tensile strain | | ISO 527-2 | 2.4 % |
Flexural modulus | | ISO 178 | 7300 Mpa |
bending strength | | ISO 178 | 215 Mpa |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of cantilever beam gap | | ISO 180/A | 6.0 kJ/m² |
Suspended wall beam without notch impact strength | | ISO 180 | 25 kJ/m² |
Filling analysis | Test Condition | Test Method | Test Result |
---|
melt viscosity | | ISO 11443 | 200 Pa·s |
Electrical performance | Test Condition | Test Method | Test Result |
---|
dielectric strength | | IEC 60243-1 | 23 KV/mm |
Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 4 |
Volume resistivity | | IEC 60093 | 1E+16 ohms·cm |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | ISO 75-2/Af | 323 °C |
Glass Transition Temperature | | ISO 11357-2 | 143 °C |
Glass Transition Temperature | | ISO 11357-2 | 147 °C |
melting temperature | | ISO 11357-3 | 343 °C |
Linear coefficient of thermal expansion | | ISO 11359-2 | 3E-05 cm/cm/°C |
Linear coefficient of thermal expansion | | ISO 11359-2 | 3E-05 cm/cm/°C |
Linear coefficient of thermal expansion | | ISO 11359-2 | 5.5E-05 cm/cm/°C |
Linear coefficient of thermal expansion | | ISO 11359-2 | 1.2E-04 cm/cm/°C |
thermal conductivity | | ISO 22007-4 | 0.30 W/m/K |
thermal conductivity | | ISO 22007-4 | 0.35 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.