Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.15 -- |
| Shrinkage rate | | % | 0.70 -- |
| Shrinkage rate | | % | 0.70 -- |
| Water absorption rate | | % | 9.0 -- |
| Water absorption rate | | % | 3.5 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | MPa | 160 160 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | | V-2 -- |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 11 12 |
| Impact strength of simply supported beam without notch | | | 无断裂 |
| Impact strength of simply supported beam without notch | | | 无断裂 |
| Charpy Notched Impact Strength | | kJ/m² | 11 12 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | MPa | 2800 2800 |
| tensile strength | Yield | MPa | 105 95.0 |
| Tensile strain | Yield | % | 7.0 6.0 |
| Tensile strain | Break | % | 25 >50 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ohms | -- 1E+12 |
| Volume resistivity | | ohms·cm | 1E+13 1E+13 |
| dielectric strength | | kV/mm | 27 27 |
| Compared to the Leakage Tracking Index (CTI) | | V | -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | °C | 135 -- |
| Heat distortion temperature | | °C | 125 -- |
| Continuous use temperature | | °C | 80.0to100 -- |
| Continuous use temperature | | °C | 120 -- |
| Glass Transition Temperature | | °C | 160 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 6E-05 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 6E-05 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.