'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
ABS Generic ABS+PC - Glass Fiber Generic
Properties:
Filler glass fiber reinforced material
Product Description
Certificates(0)
Datasheet
Product Description
| Properties: | Filler | glass fiber reinforced material |
Certificates
No Data...
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 6.9to10 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 25to40 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 58to130 | J/m |
| 23°C | ISO 180 | 4.0to14 | kJ/m² | |
| Suspended wall beam without notch impact strength | 23°C | ASTM D256 | 310to800 | J/m |
| 23°C | ISO 180 | 21to38 | kJ/m² | |
| Dart impact | 23°C | ASTM D3763 | 13.3to35.0 | J |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| Hot filament ignition temperature | IEC 60695-2-13 | 642to755 | °C | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Tensile modulus | 23°C | ASTM D638 | 3450to9650 | MPa |
| 23°C | ISO 527-2 | 3300to7800 | MPa | |
| bending strength | 23°C | ASTM D790 | 94.3to173 | MPa |
| 23°C | ISO 178 | 92.3to144 | MPa | |
| Yield,23°C | ASTM D790 | 101to138 | MPa | |
| Break,23°C | ASTM D790 | 99.7to142 | MPa | |
| tensile strength | Yield,23°C | ASTM D638 | 58.3to125 | MPa |
| Yield,23°C | ISO 527-2 | 58.3to95.6 | MPa | |
| Break,23°C | ASTM D638 | 48.8to110 | MPa | |
| Break,23°C | ISO 527-2 | 50.9to95.1 | MPa | |
| 23°C | ASTM D638 | 73.1to125 | MPa | |
| elongation | Yield,23°C | ASTM D638 | 2.5to5.0 | % |
| Yield,23°C | ISO 527-2 | 2.1to5.5 | % | |
| Break,23°C | ASTM D638 | 1.5to7.4 | % | |
| Break,23°C | ISO 527-2 | 2.0to5.1 | % | |
| Bending modulus | 23°C | ASTM D790 | 2450to8580 | MPa |
| 23°C | ISO 178 | 3000to8230 | MPa | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Linear coefficient of thermal expansion | TD | ASTME831 | 3.2E-5到7.3E-5 | cm/cm/°C |
| TD | ISO 11359-2 | 7.9E-5到8.3E-5 | cm/cm/°C | |
| Hot deformation temperature | 0.45MPa,Unannealed | ASTM D648 | 92.0to139 | °C |
| 0.45MPa,Unannealed | ISO 75-2/B | 89.0to140 | °C | |
| 1.8MPa,Unannealed | ASTM D648 | 87.5to136 | °C | |
| 1.8MPa,Unannealed | ISO 75-2/A | 112to124 | °C | |
| Vicat softening temperature | -- | ASTM D1525 | 101to144 | °C |
| -- | ISO 306 | 99.4to140 | °C | |
| Linear coefficient of thermal expansion | TD | ASTM D696 | 6.5E-5到8.2E-5 | cm/cm/°C |
| MD | ASTM D696 | 2.9E-5到6.1E-5 | cm/cm/°C | |
| MD | ASTME831 | 2.9E-5到7.7E-5 | cm/cm/°C | |
| MD | ISO 11359-2 | 1.7E-5到7.7E-5 | cm/cm/°C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Shrinkage rate | 23°C | ISO 294-4 | 0.20to0.46 | % |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.098to0.10 | % |
| 23°C,24hr | ISO 62 | 0.29to0.60 | % | |
| Equilibrium,23°C,50%RH | ISO 62 | 0.20to0.25 | % | |
| density | -- | ASTM D792 | 1.17to1.43 | g/cm³ |
| 23°C | ISO 1183 | 1.17to1.43 | g/cm³ | |
| melt mass-flow rate | 250°C/2.16kg | ASTM D1238 | 2.3to4.1 | g/10min |
| 260°C/5.0kg | ISO 1133 | 9.7to30 | g/10min | |
| Melt Volume Flow Rate (MVR) | 260°C/5.0kg | ISO 1133 | 14.8to20.0 | cm³/10min |
| Shrinkage rate | MD:23°C | ASTM D955 | 0.15to0.43 | % |
| TD:23°C | ASTM D955 | 0.25to0.65 | % | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Surface resistivity | -- | ASTM D257 | 1.0E+2到2.5E+14 | ohms |
| -- | IEC 60093 | 9.8E+14到1.0E+15 | ohms | |
| Volume resistivity | 23°C | ASTM D257 | 5.1E+5到1.3E+16 | ohms·cm |
| 23°C | IEC 60093 | 1.0E+13到1.0E+15 | ohms·cm | |
| Dielectric strength | 23°C | ASTM D149 | 26to36 | kV/mm |
| Arc resistance | ASTM D495 | 69.0to106 | sec | |
| Compared to the anti leakage trace index | IEC 60112 | PLC 2 | ||
| High arc combustion index | HAI | UL 746 | PLC 0 | |
| High voltage arc tracing rate | HVTR | UL 746 | PLC 4 | mm/min |
| Hot wire ignition | HWI | UL 746 | PLC 0 | sec |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | 23°C | ASTM D785 | 111to120 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.