ABS Generic ABS+PC - Glass Fiber Generic
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodGeneric/Generic ABS+PC - Glass Fiber
Charpy Notched Impact Strength23°CISO 1796.9to10 kJ/m²
Impact strength of cantilever beam gap23°CASTM D25658to130 J/m
Suspended wall beam without notch impact strength23°CISO 18021to38 kJ/m²
Impact strength of cantilever beam gap23°CISO 1804.0to14 kJ/m²
Suspended wall beam without notch impact strength23°CASTM D256310to800 J/m
Dart impact23°CASTM D376313.3to35.0 J
Impact strength of simply supported beam without notch23°CISO 17925to40 kJ/m²
hardnessTest ConditionTest MethodGeneric/Generic ABS+PC - Glass Fiber
Rockwell hardness23°CASTM D785111to120
Electrical performanceTest ConditionTest MethodGeneric/Generic ABS+PC - Glass Fiber
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 2
Hot wire ignition (HWI)HWIUL 746PLC 0 sec
Surface Resistivity--ASTM D2571.0E+2到2.5E+14 ohms
High Voltage Arc Traceability Rate (HVTR)HVTRUL 746PLC 4 mm/min
High arc combustion index (HAI)HAIUL 746PLC 0
Volume resistivity23°CASTM D2575.1E+5到1.3E+16 ohms·cm
23°CIEC 600931.0E+13到1.0E+15 ohms·cm
dielectric strength23°CASTM D14926to36 kV/mm
Surface Resistivity--IEC 600939.8E+14到1.0E+15 ohms
arc resistanceASTM D49569.0to106 sec
Mechanical propertiesTest ConditionTest MethodGeneric/Generic ABS+PC - Glass Fiber
bending strength23°CASTM D79094.3to173 MPa
tensile strength 断裂,23°CASTM D63848.8to110 MPa
Tensile modulus23°CISO 527-23300to7800 MPa
tensile strength 屈服,23°CISO 527-258.3to95.6 MPa
bending strength屈服,23°CASTM D790101to138 MPa
elongation屈服,23°CISO 527-22.1to5.5 %
断裂,23°CISO 527-22.0to5.1 %
bending strength断裂,23°CASTM D79099.7to142 MPa
Flexural modulus23°CISO 1783000to8230 MPa
tensile strength 23°CASTM D63873.1to125 MPa
Tensile modulus23°CASTM D6383450to9650 MPa
tensile strength 断裂,23°CISO 527-250.9to95.1 MPa
Flexural modulus23°CASTM D7902450to8580 MPa
elongation屈服,23°CASTM D6382.5to5.0 %
tensile strength 屈服,23°CASTM D63858.3to125 MPa
bending strength23°CISO 17892.3to144 MPa
elongation断裂,23°CASTM D6381.5to7.4 %
flammabilityTest ConditionTest MethodGeneric/Generic ABS+PC - Glass Fiber
Hot filament ignition temperatureIEC 60695-2-13642to755 °C
physical property Test ConditionTest MethodGeneric/Generic ABS+PC - Glass Fiber
melt mass-flow rate250°C/2.16kgASTM D12382.3to4.1 g/10min
Shrinkage rate23°CISO 294-40.20to0.46 %
density23°CISO 11831.17to1.43 g/cm³
Shrinkage rateMD:23°CASTM D9550.15to0.43 %
Water absorption rate23°C,24hrISO 620.29to0.60 %
melt mass-flow rate260°C/5.0kgISO 11339.7to30 g/10min
Water absorption rate平衡,23°C,50%RHISO 620.20to0.25 %
23°C,24hrASTM D5700.098to0.10 %
density--ASTM D7921.17to1.43 g/cm³
Shrinkage rateTD:23°CASTM D9550.25to0.65 %
Melt volume flow rate260°C/5.0kgISO 113314.8to20.0 cm³/10min
Thermal performanceTest ConditionTest MethodGeneric/Generic ABS+PC - Glass Fiber
Heat distortion temperature1.8MPa,未退火，HDTASTM D64887.5to136 °C
Linear coefficient of thermal expansionTDASTM D6966.5E-5到8.2E-5 cm/cm/°C
Heat distortion temperature0.45MPa,未退火，HDTASTM D64892.0to139 °C
vicat--ASTM D1525101to144 °C
Linear coefficient of thermal expansionTDASTME8313.2E-5到7.3E-5 cm/cm/°C
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B89.0to140 °C
1.8MPa,未退火，HDTISO 75-2/A112to124 °C
Linear coefficient of thermal expansionMDASTM D6962.9E-5到6.1E-5 cm/cm/°C
MDISO 11359-21.7E-5到7.7E-5 cm/cm/°C
MDASTME8312.9E-5到7.7E-5 cm/cm/°C
TDISO 11359-27.9E-5到8.3E-5 cm/cm/°C
vicat--ISO 30699.4to140 °C