Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
density | | | 1.70to1.85 g/cm³ |
Shrinkage rate | | | 0.20to0.35 % |
Outdoor applicability | | UL 746C | f1 |
flammability | Test Condition | Test Method | Test Result |
---|
UL flame retardant rating | | UL 94 | HB |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
bending strength | Compression Molded | ASTM D790 | 68.9 MPa |
compressive strength | | ASTM D695 | 121 MPa |
Poisson's ratio | | | 0.30 |
Tensile modulus | | ASTM D638 | 11000 MPa |
tensile strength | Compression Molded | ASTM D638 | 20.7 MPa |
Flexural modulus | Compression Molded | ASTM D790 | 9650 MPa |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of cantilever beam gap | Compression Molded | ASTM D256 | 310 J/m |
Suspended wall beam without notch impact strength | Compression Molded | ASTM D4812 | 360 J/m |
Electrical performance | Test Condition | Test Method | Test Result |
---|
arc resistance | | ASTM D495 | 180 sec |
dielectric strength | | ASTM D149 | 15 kV/mm |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Linear coefficient of thermal expansion | | | 2.5E-05 cm/cm/°C |
Linear coefficient of thermal expansion | | | 3.5E-05 cm/cm/°C |
thermal conductivity | | | 0.30 W/m/K |
RTI Elec | | UL 746 | 130 °C |
RTI Imp | | UL 746 | 130 °C |
RTI Str | | UL 746 | 130 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.