Plastomer, Ethylene-based Premi-Glas® 1200H-10 USA Premix
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | USA Premix/Premi-Glas® 1200H-10 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 模压成型 | ASTM D4812 | 360 J/m |
| Impact strength of cantilever beam gap | 模压成型 | ASTM D256 | 310 J/m |
| Mechanical properties | Test Condition | Test Method | USA Premix/Premi-Glas® 1200H-10 |
|---|---|---|---|
| Flexural modulus | 模压成型 | ASTM D790 | 9650 MPa |
| compressive strength | ASTM D695 | 121 MPa | |
| Tensile modulus | ASTM D638 | 11000 MPa | |
| bending strength | 模压成型 | ASTM D790 | 68.9 MPa |
| tensile strength | 模压成型 | ASTM D638 | 20.7 MPa |
| Poisson's ratio | 0.30 |
| Electrical performance | Test Condition | Test Method | USA Premix/Premi-Glas® 1200H-10 |
|---|---|---|---|
| dielectric strength | ASTM D149 | 15 kV/mm | |
| arc resistance | ASTM D495 | 180 sec |
| flammability | Test Condition | Test Method | USA Premix/Premi-Glas® 1200H-10 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | USA Premix/Premi-Glas® 1200H-10 |
|---|---|---|---|
| density | 1.70to1.85 g/cm³ | ||
| Shrinkage rate | MD | 0.20to0.35 % | |
| Outdoor applicability | UL 746C | f1 |
| Thermal performance | Test Condition | Test Method | USA Premix/Premi-Glas® 1200H-10 |
|---|---|---|---|
| thermal conductivity | 0.30 W/m/K | ||
| Linear coefficient of thermal expansion | MD | 2.5E-05 cm/cm/°C | |
| RTI Imp | UL 746 | 130 °C | |
| Linear coefficient of thermal expansion | TD | 3.5E-05 cm/cm/°C | |
| RTI Str | UL 746 | 130 °C | |
| RTI Elec | UL 746 | 130 °C |