PA6

PA6 PA NE 30-3M Poly Plastic

Properties:
Filler glass fiber reinforced material
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	20°C		70 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-40°C		50 kJ/m²
Charpy Notched Impact Strength	20°C		7.0 kJ/m²

mechanical properties	Test Condition	Test Result
bending strength		255 MPa
Bending modulus	23°C	9000 MPa
Tensile strain	Break	6.0 %
tensile strength	Yield	170 MPa

thermal performance	Test Condition	Test Method	Test Result
Melting temperature			219 °C
Hot deformation temperature	1.8MPa,Unannealed		205 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH		1.9 %
	Water absorption rate	Saturation,23°C		6.1 %
	Water absorption rate	Water absorption rate	23°C,24hr	ISO 62	0.85 %
Shrinkage rate			0.30to0.50 %
density			1.42 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity	--2		1E+15 ohms
Volume resistivity	--3		1E+15 ohms·cm
Volume resistivity	Volume resistivity	--2		1E+17 ohms·cm
Surface resistivity	--3		1E+13 ohms
Dielectric strength	--3		14to19 kV/mm
Dielectric strength	Dielectric strength	--2		22to25 kV/mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.