Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 PA NE 30-3M Poly Plastic
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Poly Plastic/ PA NE 30-3M |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -40°C | 50 kJ/m² | |
| 20°C | 70 kJ/m² | ||
| Charpy Notched Impact Strength | 20°C | 7.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Poly Plastic/ PA NE 30-3M |
|---|---|---|---|
| Volume resistivity | --3 | 1E+15 ohms·cm | |
| --2 | 1E+17 ohms·cm | ||
| Surface Resistivity | --3 | 1E+13 ohms | |
| --2 | 1E+15 ohms | ||
| dielectric strength | --3 | 14to19 kV/mm | |
| --2 | 22to25 kV/mm |
| Mechanical properties | Test Condition | Test Method | Poly Plastic/ PA NE 30-3M |
|---|---|---|---|
| Flexural modulus | 23°C | 9000 MPa | |
| Tensile strain | 断裂 | 6.0 % | |
| bending strength | 255 MPa | ||
| tensile strength | 屈服 | 170 MPa |
| physical property | Test Condition | Test Method | Poly Plastic/ PA NE 30-3M |
|---|---|---|---|
| Shrinkage rate | 0.30to0.50 % | ||
| density | 1.42 g/cm³ | ||
| Water absorption rate | 饱和,23°C | 6.1 % | |
| 23°C,24hr | ISO 62 | 0.85 % | |
| 平衡,23°C,50%RH | 1.9 % |
| Thermal performance | Test Condition | Test Method | Poly Plastic/ PA NE 30-3M |
|---|---|---|---|
| melting temperature | 219 °C | ||
| Heat distortion temperature | 1.8MPa,未退火，HDT | 205 °C |