Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.50 -- |
| Water absorption rate | | % | 0.18 -- |
| Water absorption rate | | % | 0.72 -- |
| Water absorption rate | | % | 0.17 -- |
| Water absorption rate | | mg | 16.0 -- |
| Water absorption rate | | mg | 32.00.36 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | | 84 -- |
| ball-indentation hardness | | MPa | 140 -- |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | HB -- |
| UL flame retardant rating | | | HB -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | MPa | 55.0 -- |
| Tensile strain | Break | % | 10 10 |
| compression stress | | MPa | 26.0 -- |
| compression stress | | MPa | 44.0 -- |
| compression stress | | MPa | 77.0 -- |
| Tensile modulus | | MPa | 3100 3100 |
| tensile strength | Break | MPa | 55.0 55.0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 3.0 -- |
| Impact strength of simply supported beam without notch | | kJ/m² | 30 -- |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ohms | >1.0E+13 >1.0E+13 |
| Volume resistivity | | ohms·cm | >1.0E+14 >1.0E+14 |
| dielectric strength | | kV/mm | 20 20 |
| relative permittivity | | | 3.60 3.60 |
| relative permittivity | | | 3.60 3.60 |
| Dissipation Factor | | | 3E-03 3E-03 |
| Dissipation Factor | | | 8E-03 8E-03 |
| Compared to the Leakage Tracking Index (CTI) | | V | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | °C | 100 -- |
| melting temperature | | °C | 180 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 1.1E-04 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 1.2E-04 -- |
| thermal conductivity | | W/m/K | 0.31 -- |
| Minimum operating temperature | | °C | -20 -- |
| maximum service temperature | | °C | 90 -- |
| maximum service temperature | | °C | 105 -- |
| maximum service temperature | | °C | 150 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.