POM Homopolymer Quadrant EPP ERTACETAL® H-TF Mitsubishi Chemical Advanced Materials
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP ERTACETAL® H-TF |
|---|---|---|---|
| Charpy Notched Impact Strength | kJ/m² | 3.0 -- | |
| Impact strength of simply supported beam without notch | kJ/m² | 30 -- |
| hardness | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP ERTACETAL® H-TF |
|---|---|---|---|
| ball-indentation hardness | 10.0mm | MPa | 140 -- |
| Rockwell hardness | M计秤,10.0mm | 84 -- |
| Mechanical properties | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP ERTACETAL® H-TF |
|---|---|---|---|
| compression stress | 2%应变 | MPa | 44.0 -- |
| 5%应变 | MPa | 77.0 -- | |
| tensile strength | 断裂 | MPa | 55.0 55.0 |
| compression stress | 1%应变 | MPa | 26.0 -- |
| Tensile modulus | MPa | 3100 3100 | |
| Tensile strain | 断裂 | % | 10 10 |
| tensile strength | -- | MPa | 55.0 -- |
| Electrical performance | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP ERTACETAL® H-TF |
|---|---|---|---|
| Surface Resistivity | ohms | >1.0E+13 >1.0E+13 | |
| relative permittivity | 100Hz | 3.60 3.60 | |
| 1MHz | 3.60 3.60 | ||
| Dissipation Factor | 1MHz | 8E-03 8E-03 | |
| dielectric strength | 1.00mm,在油中 | kV/mm | 20 20 |
| Dissipation Factor | 100Hz | 3E-03 3E-03 | |
| Volume resistivity | ohms·cm | >1.0E+14 >1.0E+14 | |
| Compared to the Leakage Tracking Index (CTI) | V | PLC 0 |
| flammability | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP ERTACETAL® H-TF |
|---|---|---|---|
| UL flame retardant rating | 6.0mm | HB -- | |
| 3.0mm | HB -- |
| physical property | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP ERTACETAL® H-TF |
|---|---|---|---|
| density | g/cm³ | 1.50 -- | |
| Water absorption rate | 饱和,23°C | % | 0.72 -- |
| 23°C,3.00mm2 | mg | 16.0 -- | |
| 平衡,23°C,50%RH | % | 0.17 -- | |
| 23°C,3.00mm3 | mg | 32.00.36 -- | |
| 23°C,24hr | % | 0.18 -- |
| Thermal performance | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP ERTACETAL® H-TF |
|---|---|---|---|
| maximum service temperature | forshortperiods | °C | 150 -- |
| Linear coefficient of thermal expansion | MD：23到100°C | cm/cm/°C | 1.2E-04 -- |
| melting temperature | °C | 180 -- | |
| maximum service temperature | continuously:for20,000h | °C | 90 -- |
| Linear coefficient of thermal expansion | MD：23到60°C | cm/cm/°C | 1.1E-04 -- |
| Heat distortion temperature | 1.8MPa,未退火，HDT | °C | 100 -- |
| maximum service temperature | continuously:for5,000h | °C | 105 -- |
| thermal conductivity | 23°C | W/m/K | 0.31 -- |
| Minimum operating temperature | °C | -20 -- |