PVC

PVC Sekisui PVC HA-24F Sekisui (Hong Kong) Limited

Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		JISK7111	25 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch		JISK7111	25 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus		JISK7171	2750 MPa
Tensile strain	Break	JISK7113	80 %
tensile strength	Yield	JISK7113	58.0 MPa
bending strength		JISK7171	86.0 MPa
bending strength	bending strength		JISK7171	86.0 MPa
tensile strength	Yield	JISK7113	58.0 MPa
Tensile strain	Break	JISK7113	80 %
Bending modulus		JISK7171	2750 MPa

thermal performance	Test Condition	Test Method	Test Result
Heat loss		JISK6720-2	<0.3 wt%
Linear coefficient of thermal expansion	MD	ASTM D696	7.0E-5到7.5E-5 cm/cm/°C
Vicat softening temperature		JISK7206	103 °C
Hot deformation temperature	1.8MPa,Unannealed	JISK7191-1	85.0 °C
	Hot deformation temperature	0.45MPa,Unannealed	JISK7207	95.0 °C
		Hot deformation temperature	0.45MPa,Unannealed	JISK7207	95.0 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	JISK7191-1	85.0 °C
Vicat softening temperature		JISK7206	103 °C
Linear coefficient of thermal expansion	MD	ASTM D696	7.0E-5到7.5E-5 cm/cm/°C
Heat loss		JISK6720-2	<0.3 wt%

Physical properties	Test Condition	Test Method	Test Result
density		JISK7112	1.53 g/cm³
Chlorine content		ISO 1158	64.0 wt%
K-Value		JISK6720-2	58.0
Apparent density		JISK6720-2	0.50to0.60 g/cm³
Apparent density	Apparent density		JISK6720-2	0.50to0.60 g/cm³
density		JISK7112	1.53 g/cm³
K-Value		JISK6720-2	58.0
Chlorine content		ISO 1158	64.0 wt%

Electrical performance	Test Condition	Test Method	Test Result
Dielectric constant	1MHz		3.20to3.60
Dielectric constant	Dielectric constant	60Hz		3.08
Dielectric strength			47to63 kV/mm
Dielectric constant	1MHz		3.20to3.60
Dielectric constant	Dielectric constant	60Hz		3.08
Dielectric strength			47to63 kV/mm
Volume resistivity	23°C		1E+15 ohms·cm
Volume resistivity	Volume resistivity	23°C		1E+15 ohms·cm

Supplementary Information	Test Condition	Test Method	Test Result
temperature	弯曲 (Flex)	JISK6745	86 °C
temperature	temperature	弯曲 (Flex)	JISK6745	86 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.