PPO/PA NORYL GTX™  GTX810-1710

43
  • Properties:
    Chemical resistance
    enhance
    High temperature resistan
  • Usages:
    Casters
    fibre

Technical Data Sheet

physical property Test ConditionTest MethodTest Result
Shrinkage rate内部方法0.60 - 0.80 %
Shrinkage rate内部方法0.65 - 0.85 %
Water absorption rateASTM D5700.50 %
Water absorption rateASTM D5701.0 %
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessASTM D785119
flammabilityTest ConditionTest MethodTest Result
UL flame retardant ratingUL 94HB
Mechanical propertiesTest ConditionTest MethodTest Result
tensile strength ASTM D63889.0 Mpa
tensile strength ASTM D63888.0 Mpa
elongationASTM D63810 %
Flexural modulusASTM D7903960 Mpa
bending strengthASTM D790155 Mpa
Electrical performanceTest ConditionTest MethodTest Result
arc resistanceASTM D495PLC 6
Compared to the Leakage Tracking Index (CTI)UL 746PLC 3
High arc combustion index (HAI)UL 746PLC 0
High Voltage Arc Traceability Rate (HVTR)UL 746PLC 3
Hot wire ignition (HWI)UL 746PLC 0
injectionTest ConditionTest MethodTest Result
drying temperature95 to 105 °C
drying time3.0 to 4.0 hr
Suggested maximum moisture content0.070 %
Suggested injection volume30 to 50 %
Temperature at the rear of the barrel265 to 305 °C
Temperature in the middle of the barrel270 to 305 °C
Temperature at the front of the material cylinder275 to 305 °C
Spray nozzle temperature280 to 305 °C
Processing (melt) temperature280 to 305 °C
Temperature75 to 120 °C
Back pressure0.300 to 1.40 Mpa
screw speed20 to 100 rpm
Exhaust hole depth0.013 to 0.038 mm
Thermal performanceTest ConditionTest MethodTest Result
Heat distortion temperatureASTM D648245 °C
Heat distortion temperatureASTM D648210 °C
vicatASTM D15253240 °C
Linear coefficient of thermal expansionASTM E8314.0E-5 - 5.0E-5 cm/cm/°C
RTI ElecUL 74650.0 °C
RTI ImpUL 74650.0 °C
RTIUL 74650.0 °C
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.