PPO/PA GTX810-1710 SABIC INNOVATIVE US
NORYL GTX™
Casters、fibre
Chemical resistance、enhance、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/GTX810-1710 |
|---|---|---|---|
| Rockwell hardness | R 级 | ASTM D785 | 119 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/GTX810-1710 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 10 % |
| tensile strength | 断裂 | ASTM D638 | 88.0 Mpa |
| bending strength | 屈服, 100 mm 跨距 | ASTM D790 | 155 Mpa |
| tensile strength | 屈服 | ASTM D638 | 89.0 Mpa |
| Flexural modulus | 100 mm 跨距 | ASTM D790 | 3960 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/GTX810-1710 |
|---|---|---|---|
| Hot wire ignition (HWI) | UL 746 | PLC 0 | |
| arc resistance | ASTM D495 | PLC 6 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 3 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 | |
| High arc combustion index (HAI) | UL 746 | PLC 0 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/GTX810-1710 |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/GTX810-1710 |
|---|---|---|---|
| Shrinkage rate | 横向流动 : 3.20 mm | 内部方法 | 0.65 - 0.85 % |
| Water absorption rate | 24 hr, 50% RH | ASTM D570 | 0.50 % |
| 平衡, 50% RH | ASTM D570 | 1.0 % | |
| Shrinkage rate | 流动 : 3.20 mm | 内部方法 | 0.60 - 0.80 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/GTX810-1710 |
|---|---|---|---|
| vicat | ASTM D15253 | 240 °C | |
| Linear coefficient of thermal expansion | -20 到 150°C，流动 | ASTM E831 | 4.0E-5 - 5.0E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 210 °C |
| RTI Imp | UL 746 | 50.0 °C | |
| RTI | UL 746 | 50.0 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 245 °C |
| RTI Elec | UL 746 | 50.0 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/GTX810-1710 |
|---|---|---|---|
| screw speed | 20 to 100 rpm | ||
| Suggested maximum moisture content | 0.070 % | ||
| Processing (melt) temperature | 280 to 305 °C | ||
| drying temperature | 95 to 105 °C | ||
| Suggested injection volume | 30 to 50 % | ||
| drying time | 3.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 270 to 305 °C | ||
| Temperature at the rear of the barrel | 265 to 305 °C | ||
| Exhaust hole depth | 0.013 to 0.038 mm | ||
| Temperature at the front of the material cylinder | 275 to 305 °C | ||
| Back pressure | 0.300 to 1.40 Mpa | ||
| Temperature | 75 to 120 °C | ||
| Spray nozzle temperature | 280 to 305 °C |