Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.56 -- |
| Shrinkage rate | | % | 0.40到1.0 -- |
| Water absorption rate | | % | 6.0 -- |
| Water absorption rate | | % | 2.0 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | | 110 90 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | HB -- |
| UL flame retardant rating | | | HB -- |
| Hot filament ignition temperature | | °C | 650 -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | Break | % | 2.0 4.0 |
| Flexural modulus | | MPa | 13500 9500 |
| bending strength | Break | MPa | 200 130 |
| tensile strength | Break | MPa | 210 130 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | J/m | 90 150 |
| Impact strength of cantilever beam gap | | J/m | 180 240 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ohms | 1E+14 1E+13 |
| Volume resistivity | | ohms·cm | 1E+15 1E+12 |
| Dissipation Factor | | | 0.020 0.12 |
| dielectric strength | | kV/mm | 34 24 |
| | | 3.80 4.20 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | °C | 190 -- |
| Crystallization peak temperature | | °C | 220 -- |
| | cm/cm/°C | 5E-05 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.