PA6 Niretan B F50 Soredi S.p.a.
--
--
Filler, glass fiber reinforced material, 50%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Soredi S.p.a./Niretan B F50 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -20°C,3.20mm | J/m | 90 150 |
| 23°C,3.20mm | J/m | 180 240 |
| hardness | Test Condition | Test Method | Soredi S.p.a./Niretan B F50 |
|---|---|---|---|
| Rockwell hardness | R级 | 110 90 |
| Mechanical properties | Test Condition | Test Method | Soredi S.p.a./Niretan B F50 |
|---|---|---|---|
| tensile strength | 断裂 | MPa | 210 130 |
| Flexural modulus | MPa | 13500 9500 | |
| bending strength | 断裂 | MPa | 200 130 |
| elongation | 断裂 | % | 2.0 4.0 |
| Electrical performance | Test Condition | Test Method | Soredi S.p.a./Niretan B F50 |
|---|---|---|---|
| Surface Resistivity | ohms | 1E+14 1E+13 | |
| dielectric strength | 1.00mm | kV/mm | 34 24 |
| Volume resistivity | ohms·cm | 1E+15 1E+12 | |
| relative permittivity | 1MHz | 3.80 4.20 | |
| Dissipation Factor | 1MHz | 0.020 0.12 |
| flammability | Test Condition | Test Method | Soredi S.p.a./Niretan B F50 |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | HB -- | |
| 1.6mm | HB -- | ||
| Hot filament ignition temperature | 2.0mm | °C | 650 -- |
| physical property | Test Condition | Test Method | Soredi S.p.a./Niretan B F50 |
|---|---|---|---|
| Shrinkage rate | MD | % | 0.40to1.0 -- |
| density | g/cm³ | 1.56 -- | |
| Water absorption rate | 平衡,23°C,50%RH | % | 2.0 -- |
| 23°C,24hr | % | 6.0 -- |
| Thermal performance | Test Condition | Test Method | Soredi S.p.a./Niretan B F50 |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：23到55°C | cm/cm/°C | 5E-05 -- |
| Heat distortion temperature | 1.8MPa,未退火，HDT | °C | 190 -- |
| Crystallization peak temperature | DSC | °C | 220 -- |