Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.27 g/cm³ |
| Shrinkage rate | | | 0.40to0.80 % |
| Water absorption rate | | | 2.6 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 102 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Burning wire flammability index | | IEC 60695-2-12 | 650 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 6500 MPa |
| tensile strength | Break | ISO 527-2 | 115 MPa |
| Tensile strain | Break | ISO 527-2 | 3.5 % |
| Flexural modulus | | ISO 178 | 5500 MPa |
| bending strength | | ISO 178 | 200 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | 30 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | DIN 53482 | 1E+12 ohms |
| Volume resistivity | | DIN 53482 | 1E+15 ohms·cm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 200 °C |
| Heat distortion temperature | | ISO 75-2/A | 190 °C |
| melting temperature | | ISO 3146 | 220 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.