Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.56 g/cm³ |
| Shrinkage rate | | ISO 294-4 | 0.76 % |
| Shrinkage rate | | ISO 294-4 | 0.33 % |
| Water absorption rate | | ISO 62 | 4.5 % |
| Water absorption rate | | ISO 62 | 1.4 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning wire flammability index | | IEC 60695-2-12 | 700 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 725 °C |
| UL flame retardant rating | | IEC 60695-11-10,-20 | HB |
| UL flame retardant rating | | IEC 60695-11-10,-20 | HB |
| Burning wire flammability index | | IEC 60695-2-12 | 700 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 725 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Break | ISO 527-2 | 3.0 % |
| Flexural modulus | | ISO 178 | 13000 MPa |
| bending strength | | ISO 178 | 310 MPa |
| Tensile modulus | | ISO 527-2 | 16500 MPa |
| tensile strength | Break | ISO 527-2 | 220 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 15 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 20 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 95 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 100 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | -- ohms |
| Volume resistivity | | IEC 60093 | 1E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 35 kV/mm |
| relative permittivity | | IEC 60250 | 3.50 |
| relative permittivity | | IEC 60250 | 5.20 |
| Dissipation Factor | | IEC 60250 | 5E-03 |
| Dissipation Factor | | IEC 60250 | 0.015 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 220 °C |
| Heat distortion temperature | | ISO 75-2/A | 210 °C |
| melting temperature | | ISO 11357-3 | 220 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.