PA6 K224-G0 DSM Additive Manufacturing
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DSM Additive Manufacturing/ K224-G0 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 20 kJ/m² |
| -30°C | ISO 179/1eA | 15 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 100 kJ/m² |
| -30°C | ISO 179/1eU | 95 kJ/m² |
| Electrical performance | Test Condition | Test Method | DSM Additive Manufacturing/ K224-G0 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 35 kV/mm | |
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 3.50 |
| Dissipation Factor | 100Hz | IEC 60250 | 5E-03 |
| relative permittivity | 1MHz | IEC 60250 | 5.20 |
| Surface Resistivity | IEC 60093 | -- ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.015 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| Mechanical properties | Test Condition | Test Method | DSM Additive Manufacturing/ K224-G0 |
|---|---|---|---|
| Tensile strain | 断裂 | ISO 527-2 | 3.0 % |
| Tensile modulus | ISO 527-2 | 16500 MPa | |
| tensile strength | 断裂 | ISO 527-2 | 220 MPa |
| Flexural modulus | ISO 178 | 13000 MPa | |
| bending strength | ISO 178 | 310 MPa |
| flammability | Test Condition | Test Method | DSM Additive Manufacturing/ K224-G0 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | IEC 60695-11-10,-20 | HB |
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 725 °C |
| UL flame retardant rating | 1.5mm | IEC 60695-11-10,-20 | HB |
| Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 700 °C |
| Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 725 °C |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 700 °C |
| physical property | Test Condition | Test Method | DSM Additive Manufacturing/ K224-G0 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.76 % |
| MD | ISO 294-4 | 0.33 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 1.4 % |
| 饱和,23°C | ISO 62 | 4.5 % | |
| density | ISO 1183 | 1.56 g/cm³ |
| Thermal performance | Test Condition | Test Method | DSM Additive Manufacturing/ K224-G0 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 220 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 220 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 210 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1E-05 cm/cm/°C |
| TD | ISO 11359-2 | 5E-05 cm/cm/°C |