Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.46 g/cm³ |
| Water absorption rate | | ASTM D570 | 0.040 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 90 |
| Shore hardness | | ASTM D2240 | 84 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| limiting pv value | | | 142000 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Break | ASTM D638 | 172 MPa |
| elongation | Break | ASTM D638 | 2.0 % |
| Flexural modulus | | ASTM D790 | 12400 MPa |
| bending strength | Yield | ASTM D790 | 248 MPa |
| compressive strength | | ASTM D695 | 221 MPa |
| shear strength | | ASTM D732 | 138 MPa |
| coefficient of friction | Steel - Dynamic | ASTM D1894 | 0.17 |
| coefficient of friction | Steel - Static | ASTM D1894 | 0.11 |
| Tensile modulus | | ASTM D638 | 12400 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 53 J/m |
| Suspended wall beam without notch impact strength | | ASTM D256 | 640 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTM D257 | <1.0E+8 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 260 °C |
| Glass Transition Temperature | | DSC | 160 °C |
| melting temperature | | DSC | 360 °C |
| Linear coefficient of thermal expansion | | TMA | 4.5E-05 cm/cm/°C |
| thermal conductivity | | ASTMC177 | 0.25 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.