Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.19 -- |
| Shrinkage rate | | % | 0.85到1.0 -- |
| Water absorption rate | | % | 1.3 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | | 122 105 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | HB -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | MPa | 4500 2900 |
| bending strength | | MPa | 160 80.0 |
| Tensile modulus | | MPa | 5000 3100 |
| tensile strength | | MPa | 100 60.0 |
| elongation | Break | % | 6.0 8.0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | J/m | 70 140 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | 1E+15 -- |
| dielectric strength | | kV/mm | 21 -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | °C | 214到220 -- |
| | cm/cm/°C | 3E-05 -- |
| | °C | 150 -- |
| Continuous use temperature | | °C | 85.0到90.0 -- |
| | °C | 190 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.