PP TRANSMARE® 35HGF30-0.001

Properties:
Filler
glass fiber reinforced material
30%
filler by weight
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ISO 1183	1.12 g/cm³
melt mass-flow rate		ISO 1133	15 g/10min

hardness	Test Condition	Test Method	Test Result
Shore hardness		ISO 868	75

Mechanical properties	Test Method	Test Result
Flexural modulus	ISO 178	5450 MPa
bending strength	ISO 178	125 MPa
Tensile modulus	ISO 527-2/1	6470 MPa
tensile strength	ISO 527-2/50	90.0 MPa
Tensile strain	ISO 527-2/50	3.0 %

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179/1A	7.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179/1A	9.0 kJ/m²
Impact strength of cantilever beam gap		ISO 180/1A	7.0 kJ/m²
Impact strength of simply supported beam without notch		ISO 179/1U	33 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch		ISO 179/1U	45 kJ/m²
Impact strength of cantilever beam gap		ISO 180/1A	10 kJ/m²
Suspended wall beam without notch impact strength		ISO 180/1U	35 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength		ISO 180/1U	44 kJ/m²

Thermal performance	Test Condition	Test Method	Test Result
vicat		ISO 306/A	162 °C
Heat distortion temperature		ISO 75-2/B	156 °C
Heat distortion temperature	Heat distortion temperature		ISO 75-2/A	133 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.