Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP TRANSMARE® 35HGF30-0.001 Transmare Compounding B.V.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Transmare Compounding B.V./TRANSMARE® 35HGF30-0.001 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -40°C | ISO 180/1U | 35 kJ/m² |
| 23°C | ISO 180/1U | 44 kJ/m² | |
| Charpy Notched Impact Strength | -40°C | ISO 179/1A | 7.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 10 kJ/m² |
| -40°C | ISO 180/1A | 7.0 kJ/m² | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1A | 9.0 kJ/m² |
| Impact strength of simply supported beam without notch | -40°C | ISO 179/1U | 33 kJ/m² |
| 23°C | ISO 179/1U | 45 kJ/m² |
| hardness | Test Condition | Test Method | Transmare Compounding B.V./TRANSMARE® 35HGF30-0.001 |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 75 |
| Mechanical properties | Test Condition | Test Method | Transmare Compounding B.V./TRANSMARE® 35HGF30-0.001 |
|---|---|---|---|
| Tensile modulus | 4.00mm | ISO 527-2/1 | 6470 MPa |
| tensile strength | 断裂,4.00mm | ISO 527-2/50 | 90.0 MPa |
| Tensile strain | 断裂,4.00mm | ISO 527-2/50 | 3.0 % |
| Flexural modulus | ISO 178 | 5450 MPa | |
| bending strength | ISO 178 | 125 MPa |
| physical property | Test Condition | Test Method | Transmare Compounding B.V./TRANSMARE® 35HGF30-0.001 |
|---|---|---|---|
| density | ISO 1183 | 1.12 g/cm³ | |
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 15 g/10min |
| Thermal performance | Test Condition | Test Method | Transmare Compounding B.V./TRANSMARE® 35HGF30-0.001 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 156 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 133 °C | |
| vicat | ISO 306/A | 162 °C |