Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.02 g/cm³ |
| viscosity number | | ISO307 | >150 cm³/g |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 81 |
| | ISO2039-1 | 110 Mpa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| Burning wire flammability index | | IEC60695-2-12 | 800 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 775 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| Charpy Notched Impact Strength | | ISO179/1eA | 13 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 14 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 14 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Nominal tensile fracture strain | | ISO527-2/50 | >50 % |
| Nominal tensile fracture strain | | ISO527-2/50 | >50 % |
| Tensile strain | | ISO527-2/50 | 8.0 % |
| Tensile strain | | ISO527-2/50 | 5.5 % |
| OuterFiberStrain Atmospheric Stress | | ISO178 | 9.0 % |
| Tensile modulus | | ISO527-2 | 1400 Mpa |
| Tensile modulus | | ISO527-2 | 1270 Mpa |
| Flexural modulus | | ISO178 | 1700 Mpa |
| Bending stress | | ISO178 | 50.0 Mpa |
| Bending stress | | ISO178 | 90.0 Mpa |
| Tensile stress | | ISO527-2/50 | 60.0 Mpa |
| Tensile stress | | ISO527-2/50 | 48.0 Mpa |
| TensileCreepModule | | ISO899-1 | 1400 Mpa |
| Tensile creep modulus | | ISO899-1 | 700 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | IEC60250 | 0.012 |
| Dissipation Factor | | IEC60250 | 0.033 |
| | IEC60250 | 3.60 |
| | IEC60250 | 3.20 |
| Surface Resistivity | | IEC60093 | 1E+13 ohms |
| Volume resistivity | | IEC60093 | 1E+16 ohms·cm |
| dielectric strength | | IEC60243-1 | 27 KV/mm |
| CTI | | IEC60112 | 575 V |
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 122 °C |
| | ISO75-2/A | 108 °C |
| vicat | | ISO306/A | 135 °C |
| vicat | | ISO306/B | 130 °C |
| Glass Transition Temperature | | ISO11357-2 | 140 °C |
| TemperatureIndex | | IEC216 | 100 °C |
| | DSC | 250 °C |
| | ISO11359-2 | 9E-05 cm/cm/°C |
| | ISO11359-2 | 9E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare
View Prices