Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA12 CX9710 EVONIK GERMANY
TROGAMID®
Automotive Applications、Industrial accessories
Low temperature resistanc、Scratch resistant、Medium viscosity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | EVONIK GERMANY/CX9710 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | NoBreak |
| Charpy Notched Impact Strength | -30°C,完全断裂 | ISO179/1eA | 13 kJ/m² |
| Impact strength of simply supported beam without notch | 0°C | ISO179/1eU | NoBreak |
| Charpy Notched Impact Strength | 23°C,完全断裂 | ISO179/1eA | 14 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | NoBreak |
| Charpy Notched Impact Strength | 0°C,完全断裂 | ISO179/1eA | 14 kJ/m² |
| hardness | Test Condition | Test Method | EVONIK GERMANY/CX9710 |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO868 | 81 |
| Ball pressure hardness | ISO2039-1 | 110 Mpa |
| Electrical performance | Test Condition | Test Method | EVONIK GERMANY/CX9710 |
|---|---|---|---|
| CTI | --6 | IEC60112 | 575 V |
| dielectric strength | IEC60243-1 | 27 KV/mm | |
| Volume resistivity | IEC60093 | 1E+16 ohms·cm | |
| CTI | 解决方案A | IEC60112 | 600 V |
| Relative permittivity | 23°C,100Hz | IEC60250 | 3.60 |
| 23°C,1MHz | IEC60250 | 3.20 | |
| Dissipation Factor | 23°C,100Hz | IEC60250 | 0.012 |
| Surface Resistivity | IEC60093 | 1E+13 ohms | |
| Dissipation Factor | 23°C,1MHz | IEC60250 | 0.033 |
| Mechanical properties | Test Condition | Test Method | EVONIK GERMANY/CX9710 |
|---|---|---|---|
| Nominal tensile fracture strain | 23°C | ISO527-2/50 | >50 % |
| Flexural modulus | ISO178 | 1700 Mpa | |
| TensileCreepModule | 1hr | ISO899-1 | 1400 Mpa |
| Bending stress | -- | ISO178 | 90.0 Mpa |
| Tensile strain | 屈服,80°C | ISO527-2/50 | 5.5 % |
| Tensile stress | 屈服,80°C | ISO527-2/50 | 48.0 Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | 700 Mpa |
| Tensile strain | 屈服,23°C | ISO527-2/50 | 8.0 % |
| Bending stress | 3.5%Strain | ISO178 | 50.0 Mpa |
| Tensile stress | 屈服,23°C | ISO527-2/50 | 60.0 Mpa |
| Tensile modulus | 23°C | ISO527-2 | 1400 Mpa |
| Nominal tensile fracture strain | 80°C | ISO527-2/50 | >50 % |
| OuterFiberStrain Atmospheric Stress | ISO178 | 9.0 % | |
| Tensile modulus | 80°C | ISO527-2 | 1270 Mpa |
| flammability | Test Condition | Test Method | EVONIK GERMANY/CX9710 |
|---|---|---|---|
| Burning wire flammability index | 1.0mm | IEC60695-2-12 | 800 °C |
| Hot filament ignition temperature | 1.0mm | IEC60695-2-13 | 775 °C |
| UL flame retardant rating | 0.8mm | UL94 | HB |
| 1.6mm | UL94 | HB |
| physical property | Test Condition | Test Method | EVONIK GERMANY/CX9710 |
|---|---|---|---|
| density | 23°C | ISO1183 | 1.02 g/cm³ |
| viscosity number | ISO307 | >150 cm³/g |
| Thermal performance | Test Condition | Test Method | EVONIK GERMANY/CX9710 |
|---|---|---|---|
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/B | 122 °C |
| 1.8MPa,未退火 | ISO75-2/A | 108 °C | |
| vicat | -- | ISO306/B | 130 °C |
| Melting temperature | DSC | 250 °C | |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO11359-2 | 9E-05 cm/cm/°C |
| vicat | -- | ISO306/A | 135 °C |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO11359-2 | 9E-05 cm/cm/°C |
| Glass Transition Temperature | ISO11357-2 | 140 °C | |
| TemperatureIndex | IEC216 | 100 °C |