POM Copolymer

POM Copolymer Ekatal® H 12 Sattler KunststoffWerk GmbH

Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	4.8 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	6.3 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
bending strength	3.5%Strain	ISO 178	81.3 MPa
Bending modulus		ISO 178	2870 MPa
Tensile strain	Break	ISO 527-2	16 %
Tensile strain	Tensile strain	Yield	ISO 527-2	10 %
tensile strength	Break	ISO 527-2	71.4 MPa
tensile strength	tensile strength	Yield	ISO 527-2	72.5 MPa
Tensile modulus		ISO 527-2	3030 MPa
bending strength	--	ISO 178	104 MPa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD:52to117°C	ISO 11359-2	1.2E-04 cm/cm/°C
	Linear coefficient of thermal expansion	TD:20to52°C	ISO 11359-2	9.4E-05 cm/cm/°C
		Linear coefficient of thermal expansion	MD:52to117°C	ISO 11359-2	1E-04 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD:20to52°C	ISO 11359-2	1E-04 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	102 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	190°C/2.16kg	ISO 1133	12 g/10min
density		ISO 1183	1.42 g/cm³

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.