PA6

PA6 AURAMID PA6GF35BK ULT Aurora Manufacturing Ltd

Properties:
Filler glass fiber reinforced material 35% filler by weight
Usages:
currency
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179/B	>8.5 kJ/m²
Impact strength of cantilever beam gap		ISO 180	>6.5 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		Internal Method	HB
Burning rate		FMVSS302	<100 mm/min

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	210 MPa
Bending modulus		ISO 178	7500 MPa
Tensile strain	Break	ISO 527-2	<3.0 %
tensile strength	Yield	ISO 527-2	>145 MPa

thermal performance	Test Condition	Test Method	Test Result
Melting temperature		ISO 3146	218 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	>180 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	>200 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate			0.30to0.50 %
density		ISO 1183	1.37 g/cm³
Water absorption rate	23°C,24hr	ISO 62	1.1 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	>1.0E+13 ohms
Dielectric strength	2.00mm	IEC 60243-1	22 kV/mm

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test	H961/30	ISO 2039-1	195 MPa
Shore hardness	ShoreD	ISO 868	86
Rockwell hardness	R-Scale	ISO 2039-2	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.