Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 AURAMID PA6GF35BK ULT Aurora Manufacturing Ltd
--
currency
Filler, glass fiber reinforced material, 35%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Aurora Manufacturing Ltd/AURAMID PA6GF35BK ULT |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 180 | >6.5 kJ/m² | |
| Charpy Notched Impact Strength | ISO 179/B | >8.5 kJ/m² |
| hardness | Test Condition | Test Method | Aurora Manufacturing Ltd/AURAMID PA6GF35BK ULT |
|---|---|---|---|
| ball-indentation hardness | H961/30 | ISO 2039-1 | 195 MPa |
| Shore hardness | 邵氏D | ISO 868 | 86 |
| Rockwell hardness | R级 | ISO 2039-2 | 120 |
| Mechanical properties | Test Condition | Test Method | Aurora Manufacturing Ltd/AURAMID PA6GF35BK ULT |
|---|---|---|---|
| Tensile strain | 断裂 | ISO 527-2 | <3.0 % |
| tensile strength | 屈服 | ISO 527-2 | >145 MPa |
| Flexural modulus | ISO 178 | 7500 MPa | |
| bending strength | ISO 178 | 210 MPa |
| Electrical performance | Test Condition | Test Method | Aurora Manufacturing Ltd/AURAMID PA6GF35BK ULT |
|---|---|---|---|
| dielectric strength | 2.00mm | IEC 60243-1 | 22 kV/mm |
| Surface Resistivity | IEC 60093 | >1.0E+13 ohms |
| flammability | Test Condition | Test Method | Aurora Manufacturing Ltd/AURAMID PA6GF35BK ULT |
|---|---|---|---|
| burning rate | FMVSS302 | <100 mm/min | |
| UL flame retardant rating | 内部方法 | HB |
| physical property | Test Condition | Test Method | Aurora Manufacturing Ltd/AURAMID PA6GF35BK ULT |
|---|---|---|---|
| Shrinkage rate | 0.30to0.50 % | ||
| Water absorption rate | 23°C,24hr | ISO 62 | 1.1 % |
| density | ISO 1183 | 1.37 g/cm³ |
| Thermal performance | Test Condition | Test Method | Aurora Manufacturing Ltd/AURAMID PA6GF35BK ULT |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | >200 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | >180 °C | |
| melting temperature | ISO 3146 | 218 °C |