| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO 62 | 0.40 % |
| Water absorption rate | | ISO 62 | 0.20 % |
| viscosity number | | ISO 307 | 90.0 cm³/g |
| Shrinkage rate | | | 0.10 % |
| Shrinkage rate | | | 0.75 % |
| density | | ISO 1183 | 1.73 g/cm³ |
| Apparent density | | | 0.70to0.80 g/cm³ |
| Melt volume flow rate | | ISO 1133 | 8.50 cm³/10min |
| Shrinkage rate | | ISO 294-4 | 0.77 % |
| Shrinkage rate | | ISO 294-4 | 0.24 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | IEC 60695-11-10,-20 | HB |
| Flammability level | | IEC 60695-11-10,-20 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 70 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 60 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 10 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 18000 MPa |
| tensile strength | Break | ISO 527-2 | 170 MPa |
| Tensile strain | Break | ISO 527-2 | 1.6 % |
| Flexural modulus | | ISO 178 | 17700 MPa |
| bending strength | | ISO 178 | 270 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+13 ohms |
| Volume resistivity | | IEC 60093 | 1E+16 ohms·cm |
| relative permittivity | | IEC 60250 | 4.70 |
| relative permittivity | | IEC 60250 | 4.50 |
| Dissipation Factor | | IEC 60250 | 2E-03 |
| Dissipation Factor | | IEC 60250 | 0.015 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 3 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 221 °C |
| Heat distortion temperature | | ISO 75-2/A | 205 °C |
| melting temperature | | ISO 11357-3 | 223 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.0E-5到2.0E-5 cm/cm/°C |
| specific heat | | | 950 J/kg/°C |
| TEMPERATURE | | IEC 60216 | 140 °C |
| TEMPERATURE | | IEC 60216 | 210 °C |
| TEMPERATURE | | IEC 60216 | 160 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.