Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Apparent density | | ISO 60 | 0.82 g/cm³ |
| Shrinkage rate | | 内部方法 | 3.4 % |
| Average particle size | | ISO 13320 | 450 µm |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 59 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D621 | 9.00 % |
| Heat distortion temperature | | ASTM D621 | 4.00 % |
| Tensile modulus | | ISO 527-2 | 650 Mpa |
| Heat distortion temperature | | ASTM D621 | 8.00 % |
| film | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-3 | 37.0 Mpa |
| elongation | | ISO 527-3 | 600 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+17 ohms |
| Volume resistivity | | IEC 60093 | 1E+18 ohms·cm |
| dielectric strength | | ISO 12086 | 78 KV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | DIN 53752 | 1.2E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | | DIN 53752 | 1.4E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | | DIN 53752 | 1.7E-04 cm/cm/°C |
| thermal conductivity | | DIN 52612 | 0.22 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.