Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238, ISO 1133 | 20 g/10 min |
| Shrinkage rate | | ASTM D955 | 0.40 到 0.60 % |
| Shrinkage rate | | ASTM D955 | 0.40 到 0.60 % |
| Shrinkage rate | | ISO 294-4 | 0.40 到 0.60 % |
| Shrinkage rate | | ISO 294-4 | 0.40 到 0.60 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 119 |
| Rockwell hardness | | ISO 2039-2 | 119 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 2100 Mpa |
| Tensile modulus | | ISO 527-2/50 | 2100 Mpa |
| tensile strength | | ASTM D638 | 64.0 Mpa |
| tensile strength | | ISO 527-2/50 | 65.0 Mpa |
| tensile strength | | ASTM D638 | 64.0 Mpa |
| tensile strength | | ISO 527-2/50 | 65.0 Mpa |
| elongation | | ASTM D638 | 85 % |
| elongation | | ISO 527-2/50 | 85 % |
| Flexural modulus | | ASTM D790 | 2500 Mpa |
| Flexural modulus | | ISO 178 | 2400 Mpa |
| bending strength | | ASTM D790 | 93.0 Mpa |
| bending strength | | ISO 178 | 90.0 Mpa |
| injection | Test Condition | Test Method | Test Result |
|---|
| Hot air dryer | | | 80 °C |
| | | 80 °C |
| Hot air dryer | | | 4.0 hr |
| | | 4.0 hr |
| Suggested maximum moisture content | | | < 0.050 % |
| Temperature at the rear of the barrel | | | 250 到 270 °C |
| Temperature in the middle of the barrel | | | 260 到 280 °C |
| Temperature at the front of the material cylinder | | | 270 到 290 °C |
| Spray nozzle temperature | | | 270 到 290 °C |
| Temperature | | | 60 到 80 °C |
| Injection Pressure | | | 98.1 Mpa |
| Back pressure | | | 0.490 到 1.96 Mpa |
| screw speed | | | 50 到 150 rpm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Thermal deformation temperature under load | | ASTM D648 | 105 °C |
| Thermal deformation temperature under load | | ISO 75-2/B | 105 °C |
| Thermal deformation temperature under load | | ASTM D648 | 97.0 °C |
| Thermal deformation temperature under load | | ISO 75-2/A | 92.0 °C |
| vicat | | ISO 306/B50 | 108 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.