Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 0.930 g/cm³ |
| Water absorption rate | | ASTMD570 | <0.010 % |
| Water absorption rate | Saturation | ASTMD570 | <0.010 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ASTMD2240 | 66 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| PressureVelocity | | 内部方法 | 0.0701 MPa·m/s |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Abrasion | | ASTMD4020 | 10 |
| elongation | Break | ASTMD638 | 230 % |
| Flexural modulus | | ASTMD790 | 455 MPa |
| bending strength | Yield | ASTMD790 | 24.1 MPa |
| Compression Modulus | | ASTMD695 | 552 MPa |
| compressive strength | | ASTMD695 | 20.7 MPa |
| Tensile modulus | | ASTMD638 | 483 MPa |
| tensile strength | Ultimate | ASTMD638 | 30.3 MPa |
| shear strength | | ASTMD732 | 33.1 MPa |
| Steel - Static | 内部方法 | 0.090 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256A | 无断裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | ASTMD150 | 2.30 |
| Dissipation Factor | | ASTMD150 | 5E-04 |
| Surface Resistivity | | ASTMD257 | >1.0E+13 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 46.7 °C |
| Maximum operating temperature LongTerm, Air | | | 82 °C |
| Crystallization peak temperature | | ASTMD3418 | 135 °C |
| | ASTME831 | 2E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare