XLPE Visico™ ME4425/Ambicat™ LE4476
0
- Properties:Mechanical properties
CompareTechnical Data Sheet
| Test Condition | Test Method | Test Result | |
|---|---|---|---|
| Tensile strain | Break | ISO 527-2/250 | >300 % |
| Shore hardness | ISO 868 | 55 | |
| brittle temperature | ASTM D746 | <-76.0 °C | |
| Dissipation Factor | IEC 60250 | <1.0E-3 | |
| Degree of crosslinking | 2.0 day | ||
| <25.0 min | |||
| 1.00 hr | |||
| 7.0 day | |||
| density | ISO 1183 | 0.935 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 1.0 g/10min | |
| Environmental stress cracking resistance | IEC 60811-4-1/B | >96.0 hr | |
| Carbon black content | ISO 6964 | 2.5 % | |
| tensile strength | Yield | ISO 527-2/250 | >15.0 MPa |
| Tensile strain | Break | ISO 527-2/250 | >300 % |
| brittle temperature | ASTM D746 | <-76.0 °C | |
| thermosetting | IEC 60811-2-1 | 30 % | |
| IEC 60811-2-1 | 0.0 % | ||
| ChangeinTensileProperties | IEC 60811-1-2 | <25 % | |
| Tensile Properties Retention | >85 % | ||
| >70 % | |||
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| dielectric constant | IEC 60250 | <2.90 | |
| Dissipation Factor | IEC 60250 | <5.0E-4 | |
| Degree of crosslinking | 1.5 day | ||
| 7.0 day | |||
| <15.0 min | |||
| density | ISO 1183 | 0.923 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 1.0 g/10min | |
| Environmental stress cracking resistance | IEC 60811-4-1/B | >96.0 hr | |
| tensile strength | Yield | ISO 527-2/250 | >15.0 MPa |
| Tensile strain | Break | ISO 527-2/250 | >300 % |
| Shore hardness | ISO 868 | 52 | |
| brittle temperature | ASTM D746 | <-76.0 °C | |
| thermal creep | IEC 60811-2-1 | 0.0 % | |
| IEC 60811-2-1 | 60 % | ||
| Tensile Properties Retention | IEC 60811-1-2 | >25 % | |
| Degree of crosslinking | 7.0 day | ||
| <15.0 min | |||
| 1.00 hr | |||
| Change rate of tensile strength in air | IEC 60811-1-2 | <25 % | |
| IEC 60811-1-2 | <30 % | ||
| Volume resistivity | IEC 60093 | >1.0E+16 ohms·cm | |
| dielectric strength | IEC 60243-1 | >22 kV/mm | |
| dielectric constant | IEC 60250 | <2.30 | |
| Dissipation Factor | IEC 60250 | <5.0E-4 | |
| Degree of crosslinking | 1.5 day | ||
| thermosetting | IEC 60811-2-1 | 60 % | |
| IEC 60811-2-1 | 0.0 % | ||
| Tensile Properties Retention | IEC 60811-1-2 | >30 % | |
| Volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| dielectric strength | IEC 60243-1 | >22 kV/mm | |
| dielectric constant | IEC 60250 | <2.30 | |
| Dissipation Factor | IEC 60250 | <5.0E-4 | |
| Degree of crosslinking | 1.5 day | ||
| 6.0 day | |||
| <15.0 min | |||
| 1.00 hr | |||
| density | ISO 1183 | 0.930 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 1.0 g/10min | |
| Environmental stress cracking resistance | IEC 60811-4-1/B | >96.0 hr | |
| tensile strength | Yield | ISO 527-2/250 | >20.0 MPa |
| Degree of crosslinking | 1.00 hr | ||
| density | ISO 1183 | 0.923 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 1.0 g/10min | |
| Volume resistivity | IEC 60093 | >1.0E+16 ohms·cm | |
| dielectric strength | IEC 60243-1 | >22 kV/mm | |
| dielectric constant | IEC 60250 | <2.30 | |
| Environmental stress cracking resistance | IEC 60811-4-1/B | >96.0 hr | |
| tensile strength | Yield | ISO 527-2/250 | >15.0 MPa |
| Tensile strain | Break | ISO 527-2/250 | >300 % |
| Shore hardness | ISO 868 | 52 | |
| brittle temperature | ASTM D746 | <-76.0 °C | |
| thermosetting | IEC 60811-2-1 | 60 % | |
| IEC 60811-2-1 | 0.0 % | ||
| ChangeinTensileProperties | IEC 60811-2-1 | <25 % | |
| IEC 60811-2-1 | <30 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.