XLPE Visico™ ME4425/Ambicat™ LE4476 Borealis AG
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Test Condition | Test Method | Borealis AG/Visico™ ME4425/Ambicat™ LE4476 | |
|---|---|---|---|
| Tensile strain | 断裂 | ISO 527-2/250 | >300 % |
| Dissipation Factor | 50Hz | IEC 60250 | <5.0E-4 |
| Degree of crosslinking | 1.80mm7 | 7.0 day | |
| density | ISO 1183 | 0.923 g/cm³ | |
| Change rate of tensile strength in air | 135°C,240hr5 | IEC 60811-1-2 | <25 % |
| 150°C,168hr6 | IEC 60811-1-2 | <30 % | |
| Carbon black content | ISO 6964 | 2.5 % | |
| ChangeinTensileProperties | 135°C5 | IEC 60811-2-1 | <25 % |
| Environmental stress cracking resistance | ConditionB,50°C,10%Igepal,F20 | IEC 60811-4-1/B | >96.0 hr |
| Degree of crosslinking | 23°C,1.80mm7 | 6.0 day | |
| 90°C,1.80mm8 | 1.00 hr | ||
| dielectric constant | 50Hz | IEC 60250 | <2.30 |
| Shore hardness | 邵氏D,1秒 | ISO 868 | 52 |
| Degree of crosslinking | 700.0µm7 | 2.0 day | |
| 90°C,700.0µm8 | <15.0 min | ||
| 23°C,700.0µm7 | 1.5 day | ||
| thermosetting | 200°C3 | IEC 60811-2-1 | 60 % |
| 200°C4 | IEC 60811-2-1 | 0.0 % | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 1.0 g/10min |
| ChangeinTensileProperties | 150°C6 | IEC 60811-2-1 | <30 % |
| Volume resistivity | IEC 60093 | >1.0E+16 ohms·cm | |
| brittle temperature | ASTM D746 | <-76.0 °C | |
| Degree of crosslinking | 700.0µm8 | <25.0 min | |
| thermal creep | 200°C4 | IEC 60811-2-1 | 60 % |
| 200°C3 | IEC 60811-2-1 | 0.0 % | |
| tensile strength | 屈服 | ISO 527-2/250 | >15.0 MPa |
| ChangeinTensileProperties | 150°C | IEC 60811-1-2 | <25 % |
| dielectric strength | IEC 60243-1 | >22 kV/mm | |
| Degree of crosslinking | 1.80mm8 | 1.00 hr | |
| Tensile Properties Retention | 150°C6 | IEC 60811-1-2 | >30 % |
| --5 | >85 % | ||
| 135°C5 | IEC 60811-1-2 | >25 % | |
| --6 | >70 % | ||
| Environmental stress cracking resistance | 50°C,10%Igepal,F20 | IEC 60811-4-1/B | >96.0 hr |