PC/PTFE LNP™ LUBRICOMP™ DL4030

Properties:
Thermal stability
High temperature resistan
Usages:
Sports equipment
Electronic and electrical components
Automotive components
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
Shrinkage rate		ASTMD955	0.80to0.90 %
	Shrinkage rate		ISO294-4	0.88 %
	Shrinkage rate	Shrinkage rate		ISO294-4	0.83 %
Water absorption rate		ASTMD570	0.12 %
Water absorption rate	Water absorption rate		ISO62	0.15 %

Impact resistance	Test Method	Test Result
Suspended wall beam gap impact strength 3	ISO180/1A	29 kJ/m²
UnnotchedIzodImpactStrength3	ISO180/1U	140 kJ/m²
Dart impact equipped with measuring instruments	ASTMD3763	30.6 J
Multi axis Instrumented Impact Energy	ISO6603-2	34.1 J

Mechanical properties	Test Condition	Test Method	Test Result
Tensile strain		ISO527-2	5.5 %
elongation		ASTMD638	38 %
Flexural modulus		ASTMD790	2190 Mpa
Flexural modulus	Flexural modulus		ISO178	2400 Mpa
bending strength		ASTMD790	80.3 Mpa
Bending stress		ISO178	84.1 Mpa
		ASTMD3702Modified	0.18
			ASTMD3702Modified	0.070
Wear factor - Washer		ASTMD3702Modified	60.0 10^-10in^5-min/ft-lb-hr
Tensile modulus		ASTMD638	2070 Mpa
Tensile modulus	Tensile modulus		ISO527-2/1	2200 Mpa
tensile strength		ASTMD638	51.7 Mpa
Tensile stress		ISO527-2	53.0 Mpa
tensile strength		ASTMD638	47.6 Mpa
Tensile stress		ISO527-2	50.0 Mpa
elongation		ASTMD638	6.1 %

Thermal performance	Test Condition	Test Method	Test Result
		ASTMD648	128 °C
Hot deformation temperature 4		ISO75-2/Af	131 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.