Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PTFE DL4030 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Sports equipment、Electronic and electrical、Automotive components
Thermal stability、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/DL4030 |
|---|---|---|---|
| Suspended wall beam gap impact strength 3 | 23°C | ISO180/1A | 29 kJ/m² |
| UnnotchedIzodImpactStrength3 | 23°C | ISO180/1U | 140 kJ/m² |
| Multi axis Instrumented Impact Energy | ISO6603-2 | 34.1 J | |
| Dart impact equipped with measuring instruments | 23°C,EnergyatPeakLoad | ASTMD3763 | 30.6 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/DL4030 |
|---|---|---|---|
| elongation | 断裂 | ASTMD638 | 38 % |
| Flexural modulus | ASTMD790 | 2190 Mpa | |
| Tensile stress | 屈服 | ISO527-2 | 53.0 Mpa |
| Bending stress | ISO178 | 84.1 Mpa | |
| Dynamic | ASTMD3702Modified | 0.18 | |
| Tensile modulus | ASTMD638 | 2070 Mpa | |
| bending strength | ASTMD790 | 80.3 Mpa | |
| Static | ASTMD3702Modified | 0.070 | |
| Tensile stress | 断裂 | ISO527-2 | 50.0 Mpa |
| elongation | 屈服 | ASTMD638 | 6.1 % |
| Tensile modulus | ISO527-2/1 | 2200 Mpa | |
| tensile strength | 屈服 | ASTMD638 | 51.7 Mpa |
| Tensile strain | 屈服 | ISO527-2 | 5.5 % |
| tensile strength | 断裂 | ASTMD638 | 47.6 Mpa |
| Flexural modulus | ISO178 | 2400 Mpa | |
| Wear factor - Washer | ASTMD3702Modified | 60.0 10^-10in^5-min/ft-lb-hr |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/DL4030 |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.15 % |
| Shrinkage rate | MD:24小时 | ISO294-4 | 0.83 % |
| TD:24小时 | ISO294-4 | 0.88 % | |
| Water absorption rate | 24hr,50%RH | ASTMD570 | 0.12 % |
| Shrinkage rate | MD：24小时 | ASTMD955 | 0.80to0.90 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/DL4030 |
|---|---|---|---|
| 1.8MPa,未退火,3.20mm | ASTMD648 | 128 °C | |
| Hot deformation temperature 4 | 1.8MPa,未退火,64.0mm跨距 | ISO75-2/Af | 131 °C |