Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.41 g/cm³ |
| SpiralFlow | | 内部方法 | 9.00 cm |
| SpiralFlow | | 内部方法 | 41.0 cm |
| Shrinkage rate | | ISO294-4 | 0.70 % |
| Shrinkage rate | | ISO294-4 | 0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 88 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO527-2 | 70.0 MPa |
| Tensile strain | | ISO527-2 | 1.7 % |
| Flexural modulus | | ISO178 | 23000 MPa |
| Bending stress | | ISO178 | 380 MPa |
| Bending stress | | ISO178 | 290 MPa |
| Bending stress | | ISO178 | 190 MPa |
| Bending stress | | ISO178 | 100 MPa |
| compression stress | | ISO604 | 310 MPa |
| compression stress | | ISO604 | 210 MPa |
| Tensile modulus | | ISO527-2 | 25000 MPa |
| Tensile stress | | ISO527-2 | 270 MPa |
| Tensile stress | | ISO527-2 | 180 MPa |
| compression stress | | ISO604 | 95.0 MPa |
| compression stress | | ISO604 | 65.0 MPa |
| Tensile stress | | ISO527-2 | 120 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 7.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1U | 50 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/A | 9.0 kJ/m² |
| | ISO180 | 50 kJ/m² |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| melt viscosity | | ISO11443 | 560 Pa·s |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD4496 | 1E+05 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO11359-2 | 1.3E-05 cm/cm/°C |
| | ISO11359-2 | 4E-05 cm/cm/°C |
| | ISO75-2/Af | 383 °C |
| Glass Transition Temperature | | ISO11357-2 | 162 °C |
| melting temperature | | ISO11357-3 | 387 °C |
| | ISO11359-2 | 1E-05 cm/cm/°C |
| | ISO11359-2 | 9.5E-05 cm/cm/°C |
| thermal conductivity | | ISO22007-4 | 0.95 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.