PEKEKK VICTREX® ST™ ST45CA30 VICTREX UK
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | VICTREX UK/VICTREX® ST™ ST45CA30 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.0 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | 50 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 9.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1U | 50 kJ/m² |
| hardness | Test Condition | Test Method | VICTREX UK/VICTREX® ST™ ST45CA30 |
|---|---|---|---|
| Shore hardness | 邵氏D,23°C | ISO 868 | 88 |
| Mechanical properties | Test Condition | Test Method | VICTREX UK/VICTREX® ST™ ST45CA30 |
|---|---|---|---|
| tensile strength | 断裂,125°C | ISO 527-2 | 180 MPa |
| compression stress | 250°C | ISO 604 | 65.0 MPa |
| Tensile modulus | 23°C | ISO 527-2 | 25000 MPa |
| tensile strength | 断裂,275°C | ISO 527-2 | 70.0 MPa |
| compression stress | 120°C | ISO 604 | 210 MPa |
| bending strength | 125°C | ISO 178 | 290 MPa |
| Flexural modulus | 23°C | ISO 178 | 23000 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 1.7 % |
| bending strength | 175°C | ISO 178 | 190 MPa |
| compression stress | 23°C | ISO 604 | 310 MPa |
| tensile strength | 断裂,23°C | ISO 527-2 | 270 MPa |
| bending strength | 275°C | ISO 178 | 100 MPa |
| compression stress | 200°C | ISO 604 | 95.0 MPa |
| tensile strength | 断裂,175°C | ISO 527-2 | 120 MPa |
| bending strength | 23°C | ISO 178 | 380 MPa |
| Electrical performance | Test Condition | Test Method | VICTREX UK/VICTREX® ST™ ST45CA30 |
|---|---|---|---|
| Volume resistivity | 23°C | ASTM D4496 | 1E+05 ohms·cm |
| Filling analysis | Test Condition | Test Method | VICTREX UK/VICTREX® ST™ ST45CA30 |
|---|---|---|---|
| melt viscosity | 420°C | ISO 11443 | 560 Pa·s |
| physical property | Test Condition | Test Method | VICTREX UK/VICTREX® ST™ ST45CA30 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.70 % |
| MD | ISO 294-4 | 0.10 % | |
| spiral flow length | --4 | 内部方法 | 41.0 cm |
| --3 | 内部方法 | 9.00 cm | |
| density | ISO 1183 | 1.41 g/cm³ |
| Thermal performance | Test Condition | Test Method | VICTREX UK/VICTREX® ST™ ST45CA30 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 383 °C |
| melting temperature | ISO 11357-3 | 387 °C | |
| thermal conductivity | 23°C | ISO 22007-4 | 0.95 W/m/K |
| Linear coefficient of thermal expansion | TD:<162°C | ISO 11359-2 | 4E-05 cm/cm/°C |
| TD:>162°C | ISO 11359-2 | 9.5E-05 cm/cm/°C | |
| MD:<162°C | ISO 11359-2 | 1E-05 cm/cm/°C | |
| MD:>162°C | ISO 11359-2 | 1.3E-05 cm/cm/°C | |
| Glass Transition Temperature | ISO 11357-2 | 162 °C |