PS NORYL™ NH5020 resin

Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ASTM D792	1.11 g/cm³
density	density		ISO 1183	1.11 g/cm³
melt mass-flow rate		ASTM D1238	9.8 g/10min
Melt volume flow rate		ISO 1133	10.1 cm³/10min
Shrinkage rate		内部方法	0.50to0.70 %
Water absorption rate		ISO 62	0.25 %
Water absorption rate	Water absorption rate		ISO 62	0.050 %

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	V-2
	UL flame retardant rating		UL 94	V-0
	UL flame retardant rating	UL flame retardant rating		UL 94	5VA

Mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Break	ISO 527-2/50	77.5 MPa
elongation	Yield	ASTM D638	5.0 %
Tensile strain	Yield	ISO 527-2/50	4.8 %
elongation	Break	ASTM D638	15 %
Tensile strain	Break	ISO 527-2/50	5.7 %
Flexural modulus		ASTM D790	3000 MPa
Flexural modulus	Flexural modulus		ISO 178	2980 MPa
bending strength		ISO 178	126 MPa
bending strength	bending strength		ASTM D790	122 MPa
Tensile modulus		ASTM D638	2730 MPa
Tensile modulus	Tensile modulus		ISO 527-2/1	3060 MPa
tensile strength	Yield	ASTM D638	79.2 MPa
	tensile strength	Yield	ISO 527-2/50	80.1 MPa
	tensile strength	tensile strength	Break	ASTM D638	62.2 MPa

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ASTM D256	91 J/m
	Impact strength of cantilever beam gap		ISO 180/1A	6.1 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO 180/1A	8.1 kJ/m²
Dart impact		ASTM D3763	19.3 J
Charpy Notched Impact Strength		ISO 179/1eA	7.9 kJ/m²
Impact strength of cantilever beam gap		ASTM D256	59 J/m

Electrical performance	Test Condition	Test Method	Test Result
arc resistance		ASTM D495	PLC6
Compared to the Leakage Tracking Index (CTI)		UL 746	PLC 2
Compared to the Leakage Tracking Index (CTI)	Compared to the Leakage Tracking Index (CTI)		IEC 60112	PLC 5
High arc combustion index (HAI)		UL 746	PLC 0
High Voltage Arc Traceability Rate (HVTR)		UL 746	PLC 4
Hot wire ignition (HWI)		UL 746	PLC 0
dielectric strength		IEC 60243-1	49 kV/mm

Thermal performance	Test Condition	Test Method	Test Result
RTI Imp		UL 746	105 °C
RTI Str		UL 746	110 °C
Heat distortion temperature		ASTM D648	122 °C
	Heat distortion temperature		ASTM D648	134 °C
		Heat distortion temperature		ASTM D648	117 °C
			Heat distortion temperature		ASTM D648	123 °C
			Heat distortion temperature	Heat distortion temperature		ISO 75-2/Af	119 °C
vicat		ASTM D152510	138 °C
	vicat		ISO 306/B50	138 °C
	vicat	vicat		ISO 306/B120	139 °C
ball-indentation hardness		IEC 60695-10-2	Pass
Linear coefficient of thermal expansion		ASTME831	6.1E-05 cm/cm/°C
	Linear coefficient of thermal expansion		ISO 11359-2	6.1E-05 cm/cm/°C
		Linear coefficient of thermal expansion		ASTME831	6.8E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ISO 11359-2	6.8E-05 cm/cm/°C
RTI Elec		UL 746	110 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.