Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PS NORYL™ NH5020 resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/NORYL™ NH5020 resin |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.9 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 91 J/m |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 19.3 J |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 59 J/m |
| -30°C | ISO 180/1A | 6.1 kJ/m² | |
| 23°C | ISO 180/1A | 8.1 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC/NORYL™ NH5020 resin |
|---|---|---|---|
| elongation | 屈服 | ASTM D638 | 5.0 % |
| tensile strength | 屈服 | ASTM D638 | 79.2 MPa |
| Flexural modulus | ISO 178 | 2980 MPa | |
| Tensile strain | 屈服 | ISO 527-2/50 | 4.8 % |
| bending strength | ISO 178 | 126 MPa | |
| tensile strength | 屈服 | ISO 527-2/50 | 80.1 MPa |
| elongation | 断裂 | ASTM D638 | 15 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 122 MPa |
| Tensile modulus | ASTM D638 | 2730 MPa | |
| tensile strength | 断裂 | ASTM D638 | 62.2 MPa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 3000 MPa |
| Tensile strain | 断裂 | ISO 527-2/50 | 5.7 % |
| Tensile modulus | ISO 527-2/1 | 3060 MPa | |
| tensile strength | 断裂 | ISO 527-2/50 | 77.5 MPa |
| Electrical performance | Test Condition | Test Method | SABIC/NORYL™ NH5020 resin |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 5 | |
| dielectric strength | 3.20mm,在油中 | IEC 60243-1 | 49 kV/mm |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 0 |
| arc resistance | ASTM D495 | PLC6 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| High Voltage Arc Traceability Rate (HVTR) | PLC | UL 746 | PLC 4 |
| flammability | Test Condition | Test Method | SABIC/NORYL™ NH5020 resin |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| 2.5mm | UL 94 | 5VA | |
| 0.40mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | SABIC/NORYL™ NH5020 resin |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| Melt volume flow rate | 280°C/5.0kg | ISO 1133 | 10.1 cm³/10min |
| melt mass-flow rate | 280°C/5.0kg | ASTM D1238 | 9.8 g/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.050 % |
| 饱和,23°C | ISO 62 | 0.25 % | |
| density | ASTM D792 | 1.11 g/cm³ | |
| ISO 1183 | 1.11 g/cm³ |
| Thermal performance | Test Condition | Test Method | SABIC/NORYL™ NH5020 resin |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 123 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ISO 11359-2 | 6.8E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 122 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 6.1E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 6.1E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 134 °C |
| vicat | ASTM D152510 | 138 °C | |
| RTI Str | UL 746 | 110 °C | |
| vicat | -- | ISO 306/B120 | 139 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 6.8E-05 cm/cm/°C |
| vicat | -- | ISO 306/B50 | 138 °C |
| RTI Imp | UL 746 | 105 °C | |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 119 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 117 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| RTI Elec | UL 746 | 110 °C |