PC+Polyester XYLEX™ X7507 resin
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| OutdoorSuitability | UL 746C | f1 | |
| density | ASTM D792 | 1.20 g/cm³ | |
| ISO 1183 | 1.20 g/cm³ | ||
| melt mass-flow rate | ASTM D1238 | 8.0 g/10min | |
| Melt volume flow rate | ISO 1133 | 5.00 cm³/10min | |
| Shrinkage rate | 内部方法 | 0.50to0.80 % | |
| Water absorption rate | ISO 62 | 0.32 % | |
| ISO 62 | 0.12 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| transmissivity | ASTM D1003 | >85.0 % | |
| Haze ratio | ASTM D1003 | 1.6 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flexural modulus | ISO 178 | 2190 MPa | |
| bending strength | ISO 178 | 92.0 MPa | |
| ASTM D790 | 96.0 MPa | ||
| Tensile modulus | ASTM D638 | 2300 MPa | |
| ISO 527-2/1 | 2660 MPa | ||
| tensile strength | Yield | ASTM D638 | 61.0 MPa |
| Yield | ISO 527-2/50 | 62.0 MPa | |
| Break | ASTM D638 | 65.0 MPa | |
| Break | ISO 527-2/50 | 59.0 MPa | |
| elongation | Yield | ASTM D638 | 6.0 % |
| Tensile strain | Yield | ISO 527-2/50 | 5.4 % |
| elongation | Break | ASTM D638 | 130 % |
| Tensile strain | Break | ISO 527-2/50 | 110 % |
| Flexural modulus | ASTM D790 | 2320 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 20 kJ/m² | |
| Impact strength of cantilever beam gap | ASTM D256 | 200 J/m | |
| ASTM D256 | 990 J/m | ||
| ISO 180/1A | 6.0 kJ/m² | ||
| ISO 180/1A | 9.0 kJ/m² | ||
| Dart impact | ASTM D3763 | 79.0 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 104 °C | |
| ISO 75-2/Af | 105 °C | ||
| vicat | ASTM D152510 | 125 °C | |
| ISO 306/B50 | 125 °C | ||
| ISO 306/B120 | 127 °C | ||
| Linear coefficient of thermal expansion | ASTME831 | 6E-05 cm/cm/°C | |
| ISO 11359-2 | 6E-05 cm/cm/°C | ||
| ASTME831 | 7E-05 cm/cm/°C | ||
| ISO 11359-2 | 6.3E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.