Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

PC+Polyester XYLEX™ X7507 resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | SABIC/XYLEX™ X7507 resin |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 20 kJ/m² |
Impact strength of cantilever beam gap | -30°C | ASTM D256 | 200 J/m |
23°C | ASTM D256 | 990 J/m | |
Dart impact | 23°C,TotalEnergy | ASTM D3763 | 79.0 J |
Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 6.0 kJ/m² |
23°C | ISO 180/1A | 9.0 kJ/m² |
Mechanical properties | Test Condition | Test Method | SABIC/XYLEX™ X7507 resin |
---|---|---|---|
elongation | 屈服 | ASTM D638 | 6.0 % |
tensile strength | 屈服 | ASTM D638 | 61.0 MPa |
Flexural modulus | ISO 178 | 2190 MPa | |
Tensile strain | 屈服 | ISO 527-2/50 | 5.4 % |
bending strength | ISO 178 | 92.0 MPa | |
tensile strength | 屈服 | ISO 527-2/50 | 62.0 MPa |
elongation | 断裂 | ASTM D638 | 130 % |
bending strength | 屈服,50.0mm跨距 | ASTM D790 | 96.0 MPa |
Tensile modulus | ASTM D638 | 2300 MPa | |
tensile strength | 断裂 | ASTM D638 | 65.0 MPa |
Flexural modulus | 50.0mm跨距 | ASTM D790 | 2320 MPa |
Tensile strain | 断裂 | ISO 527-2/50 | 110 % |
Tensile modulus | ISO 527-2/1 | 2660 MPa | |
tensile strength | 断裂 | ISO 527-2/50 | 59.0 MPa |
optical performance | Test Condition | Test Method | SABIC/XYLEX™ X7507 resin |
---|---|---|---|
Haze ratio | 2540µm | ASTM D1003 | 1.6 % |
transmissivity | 2540µm | ASTM D1003 | >85.0 % |
physical property | Test Condition | Test Method | SABIC/XYLEX™ X7507 resin |
---|---|---|---|
Shrinkage rate | MD:3.20mm | 内部方法 | 0.50to0.80 % |
OutdoorSuitability | Natural | UL 746C | f1 |
melt mass-flow rate | 265°C/2.16kg | ASTM D1238 | 8.0 g/10min |
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.12 % |
饱和,23°C | ISO 62 | 0.32 % | |
density | ASTM D792 | 1.20 g/cm³ | |
ISO 1183 | 1.20 g/cm³ | ||
Melt volume flow rate | 265°C/2.16kg | ISO 1133 | 5.00 cm³/10min |
Thermal performance | Test Condition | Test Method | SABIC/XYLEX™ X7507 resin |
---|---|---|---|
vicat | -- | ISO 306/B120 | 127 °C |
Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
TD:-40到40°C | ISO 11359-2 | 6.3E-05 cm/cm/°C | |
vicat | -- | ISO 306/B50 | 125 °C |
Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 6E-05 cm/cm/°C |
MD:-40到40°C | ISO 11359-2 | 6E-05 cm/cm/°C | |
Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan,HDT | ISO 75-2/Af | 105 °C |
vicat | ASTM D152510 | 125 °C | |
Heat distortion temperature | 1.8MPa,未退火,3.20mm,HDT | ASTM D648 | 104 °C |