PA66 NILAMID® A3 W GF30 Celanese Corporation

Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ISO 1183	1.34 g/cm³
Shrinkage rate		ISO 294-4	0.40 %
Shrinkage rate	Shrinkage rate		ISO 294-4	1.20 %
Water absorption rate		ISO 62	1.80 %
Water absorption rate	Water absorption rate		ISO 62	6.00 %

Mechanical properties	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179/1eU	N/D kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch		ISO 179/1eU	N/D kJ/m²
tensile strength		ISO 527-2	185 MPa
elongation at break		ISO 527-2	3.5 %
Tensile modulus		ISO 527-2	9200 MPa
Charpy Notched Impact Strength		ISO 179/1eA	11 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179/1eA	8.0 kJ/m²

Flame retardant performance	Test Condition	Test Method	Test Result
UL flame retardant rating		UL -94	HB 1.50mm
UL flame retardant rating	UL flame retardant rating		UL -94	HB 3.00mm
Limiting Oxygen Index		ISO 4589-2	28 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		IEC 60093	1E+15 Ω.cm
Dissipation Factor		IEC 60112	550 V

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ISO 75-2/Bf	250 °C
Heat distortion temperature	Heat distortion temperature		ISO 75-2/Af	250 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.