PA66 NILAMID® A3 W GF30 Celanese Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | Celanese Corporation/NILAMID® A3 W GF30 |
|---|---|---|---|
| Tensile modulus | 23°C | ISO 527-2 | 9200 MPa |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 8.0 kJ/m² |
| 23°C | ISO 179/1eA | 11 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | N/D kJ/m² |
| tensile strength | 23°C | ISO 527-2 | 185 MPa |
| elongation at break | 23°C | ISO 527-2 | 3.5 % |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | N/D kJ/m² |
| Electrical performance | Test Condition | Test Method | Celanese Corporation/NILAMID® A3 W GF30 |
|---|---|---|---|
| Dissipation Factor | 相对漏电起痕指数 | IEC 60112 | 550 V |
| Volume resistivity | IEC 60093 | 1E+15 Ω.cm |
| Flame retardant performance | Test Condition | Test Method | Celanese Corporation/NILAMID® A3 W GF30 |
|---|---|---|---|
| Limiting Oxygen Index | ISO 4589-2 | 28 % | |
| UL flame retardant rating | UL -94 | HB 1.50mm | |
| UL -94 | HB 3.00mm |
| physical property | Test Condition | Test Method | Celanese Corporation/NILAMID® A3 W GF30 |
|---|---|---|---|
| Water absorption rate | (23°C,24hr) | ISO 62 | 1.80 % |
| Shrinkage rate | TD | ISO 294-4 | 1.20 % |
| MD | ISO 294-4 | 0.40 % | |
| density | ISO 1183 | 1.34 g/cm³ | |
| Water absorption rate | (23°C,50RH) | ISO 62 | 6.00 % |
| Thermal performance | Test Condition | Test Method | Celanese Corporation/NILAMID® A3 W GF30 |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 250 °C |
| 0.45MPa未退火，HDT | ISO 75-2/Bf | 250 °C |